交联聚苯乙烯,crosslinked polystyrene
1)crosslinked polystyrene交联聚苯乙烯
1.Micron monodispersedcrosslinked polystyrene microspheres were prepared by suspension polymerization in glucose aqueous solution with poly(vinyl alcohol)(PVA)as stabilizer.采用葡萄糖水溶液为分散介质,加入稳定剂聚乙烯醇,经悬浮聚合法合成了微米级单分散交联聚苯乙烯微球,考察了葡萄糖含量、苯乙烯用量、引发剂用量、稳定剂用量和交联剂用量对微米级单分散交联聚苯乙烯微球粒径大小及其分布的影响。
2.Furthermore batch addition of DVB and stablizer can produce monodisperse 1%～30%crosslinked polystyrene.采用分散聚合法合成粒径单分散交联聚苯乙烯微球 ,研究了交联剂用量、交联剂加入方式以及补加分散剂和交联剂对聚合物形态的影响。
3.Usingcrosslinked polystyrene as parent polymer, benzoyl peroxide groups were introduced onto the backbone of the polymer via a series of reactions.以交联聚苯乙烯为母体 ,经过大分子化学反应 ,在聚合物侧基苯环上引入了具有引发聚合活性的过氧酰基(聚合物固载引发剂 )。
英文短句/例句
1.Studies of Post-Crosslinking of Low Crosslinked Polystyrene (Ⅰ)低交联聚苯乙烯后交联的研究(Ⅰ)
2.Structure and Property Characterization of Cross-linked Polystyrene Sodium Sulfonate交联聚苯乙烯磺酸钠结构与性能表征
3.Study on New Method of Chloromethylation Reaction of Linear and Crosslinked Polystyrene;线型及交联聚苯乙烯的氯甲基化新方法的研究
4.Synthesis and Properties of Monodisperse Crosslinked Polystyrene Microspheres;单分散交联聚苯乙烯微球的合成及性能研究
5.Novel Synthesis of Salicylic Acid-Crosslinked Polystyrene Chelating Resin合成水杨酸-交联聚苯乙烯螯合树脂的新途径
6.Synthesis of Different Morphologies Monodispersed and Crosslinked PS Microspheres by Seed Swelling Polymerization种子溶胀法制备单分散交联聚苯乙烯微球
7.The Application Studies of PP Modified by Nano-CaCO_3 and CPMB Rigid Particles;纳米碳酸钙、交联聚苯乙烯刚性微粒改性聚丙烯的应用研究
8.The Study of Synthesis and Complexing Function of α-crosslinked-polystyryl-α′-phenyl-β-dioneα-交联聚苯乙烯-α′-苯基-β-二酮的合成及其络合性能的研究
9.Synchronistic Synthesis and Immobilization of Phenyl Porpherin on Crosslinked Polystyrene Microspheres在交联聚苯乙烯微球表面实现苯基卟啉的同步合成与固载
10.Preparation of CdTe-Loaded Crosslinked Polystyrene Fluorescent Microspheres by Miniemulsion Polymerization细乳液聚合制备载有CdTe的交联聚苯乙烯荧光微球
11.Study on Synthesis of Dioxomultiazamacrocycles Functionalized Cross-linked Polystyrene;二氧化氮杂冠醚功能化交联聚苯乙烯合成及其性能研究
12.Study on the preparation and structure of polystyrene porous crosslinked adsorbents交联聚苯乙烯型多孔吸附剂的制备与孔结构研究
13.Preparation and Functionalization of Three-dimensionally Ordered Macroporous Cross-linked Polystyrene三维有序交联聚苯乙烯大孔材料的制备及其功能化
14.Preparation of Narrowdisperse Crosslinked Poly (Styrene-co-Divinylbenzene) Microspheres by Precipitation Polymerization基于沉淀法制备单分散苯乙烯/二乙烯基苯交联聚合物微球
15.A New Type of Environmental Protection Adhesive of Cross-linking Polyvinyl Alcohol withToluene Diisocyanate;甲苯二异氰酸酯交联聚乙烯醇类环保粘合剂
16.Synthesis and characterization of photo-crosslinkable grafted polystyrene via atom transfer radical polymerization通过原子转移自由基聚合合成可光交联的聚苯乙烯接枝共聚物
17.Preparation and Slow Release Behavior of Porous Hydroquinone-carrying Poly (styrene-divinylbenzene) Microspheres负载对苯二酚的聚苯乙烯-二乙烯苯交联微球的制备及缓释行为(英文)
patible cross-linked polyvinyl alcohol相容的交联聚乙烯醇
相关短句/例句
Cross-linked polystyrene交联聚苯乙烯
1.Through chloromethylated and cross-linked polystyrene being moderately Friedel-Crafts post-cross linked and then aminated,a series of new macroporous resins,which have larger physical surface area and some alkalescent ion-exchanged groups,were produced.但吸附树脂交联聚苯乙烯疏水性强,水相与树脂之间的界面能较大,通过氯甲基化引入极性基团可以改善树脂的吸附性能[2]。
2.The three-dimensionally ordered macroporous cross-linked polystyrene(3DOM CLPS)with pore size in the range of 200～1020nm is prepared by the method of template-directed synthesis.利用二氧化硅模板法,采用苯乙烯-二乙烯基苯自由基共聚方法制备了孔径在200～1020nm的三维有序交联聚苯乙烯大孔材料,并在此基础上通过氯甲基化反应对所制备的有序孔材料进行孔壁功能化。
3)cross-linked polystyrene beads交联聚苯乙烯珠
4)styragel聚苯乙烯型交联共聚物
5)Crosslinked PS Microsphere交联型聚苯乙烯微球
6)hypercrosslinked polystyrene resin高交联聚苯乙烯树脂
1.The macroporoushypercrosslinked polystyrene resin synthesized in one step had many of carbonyl groups, which was indicated by the adsorption at 1704.用一步法合成高交联聚苯乙烯树脂,采用红外光谱对其结构进行表征,其红外光谱图中在1704。
延伸阅读
辐射交联聚乙烯分子式：分子量：CAS号：性质：交联聚乙烯的一种。密度0.92。热变形温度（1.87兆帕）38~79℃，连续耐热达135℃。体积电阻率>1015欧姆·厘米，介电常数2.27~7.60，介电损耗角正切0.003~0.005。击穿电压（厚3.2毫米）230~1420伏/毫米，吸水率0.01%~0.06%。可用作耐高电压、耐高频的耐热绝缘材料，用于包覆电缆电线，也可用于热收缩薄膜和套管。以高能射线：如β射线、γ射线等辐射聚乙烯使之发生交联而得。